Grade 7(Ti-0.15Pd)钛钯合金Grade 16钯钛合金
TI–PD GRADE 7 & GRADE 16Ti-0.15Pd (Grade 7)This alloy has mechanical properties similar to Commercially Pure Titanium Grade 2 but has improved resistance to general and localised crevice corrosion in a wide range °F reducing acid environments including chlorides, with a good balance °F moderate strength, reasonable ductility and excellent weldability.Ti-0.05Pd (Grade 16)Grade 16 is identical to Grade 7 with the exception that the palladium added to improve corrosion resistance is less than with Grade 7. Mechanical and physical properties, specifications and forms are all identical to those °F Grade 7.The alloy composition differs by the reduction °F Pd to 0.04-0.08%.Note: The poor availability and high cost °F palladium have led to the development °F ruthenium as an alternative alloy addition to provide similar enhancement °F corrosion resistance but at lower cost. The relevant ASTM Grades is 26 (CP Grade 2 + 0.1% Ru). Mechanical and physical properties are °F the same order as described for grades 7 and 16.CompositionC Fe N2 Pd 0.12-0,.25 % for Grade 7 and 0.04-0.08% for Grade 16O2 H2(sheet) H2(bar) Ti ~ RemSpecifications/Designations for Grades 11 and 17ASTM B265ASTM B337 Gr7 onlyASTM B338ASTM B348ASTM B363 (WPT)ASTM B381ASTM B861ASTM B862ASTM B863ASTM F467 Gr7 FastenersASTM F468 " "See also ASTM list °F B367 casting grades °F palladium containing alloys for approximate equivalent specifications to the wrought grades above. Physical Data TypicalDensity g/cm3 (lb/cu.in) 4.51 (0.162)Melting Range°C±15°C (°F) 1677 (3051)Specific Heat J/Kg/°C (BTU/lb/°F) 540 (.129)Volume Electrical Resistivity mohm.cm(mohm.in) 56 (22)Thermal Conductivity W/mk (BTU/ft h°F) 20.6 (143)Mean Thermal Exp. Coeff. 0-100°C/°C (0 - 212°F/°F) 8.6x10-6 (4.8)Mean Thermal Exp. Coeff. 0-300°C/°C (0 - 572°F/°F) 9.2x10-6 (5.1)Beta Transus °C±15°C(°F) 913 (1675)Mechanical Data Minimum TypicalTensile Strength MPa (ksi) 345 (50) 483 (70)0.2% Proof Stress MPa (ksi) 376 (40) 352 (51)Elongation over 2 inches % 20 28Elastic Modulus GPa (Msi) 103 (15)Hardness Bhn 160Specified Bend Radius Specified Bend Radius > 0.070in x Thickness 2.5Welded Bend Radius x Thickness 3Charpy,V-Notch Impact J(ft lbf) 41 (30)Forms AvailableStrip; Ingot & Bloom; Billet; Slab; Bar; Wire; Sheet; Plate; Forgings; Castings; Tube-WeldedFabricationWeldability - ExcellentForging - Rough 900°C (1650°F), Finish 843°C (1550°F)Annealing - 704°C (1300°F), 2hr, ACStress Relief Annealing - 483-538°C (900-1000°F), 45 mins.